Extruding Nylon Compound Plastic Raw Material PA66/PA6 GF25 Granules for Thermal Break Strip
Introduction of Raw Material:
PA has the advantages of high mechanical strength, high softening point, good wear resistance, self-lubrication, cushioning, sound deadening, excellent oil and chemical corrosion resistance, and good electrical insulation. Because of these superior performance, PA composite have already replaced some metals being as structural materials.
Product Description:
-PA66GF25 granules are reinforced by fiberglass. The final product performance of this raw material can meet the national standard.
-TPA66GF25 granules are based on PA66 resin. Then the granules are formed by twin-screw extrusion machine after adding fiberglass, efficient flame retardants and various additives.
Polywell PA66 Granules Performance Table
| NO. | Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| | Material Properties |
| 1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| 2 | Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
| 3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| 4 | Melting point | ºC | ≥240 | ≥240 |
| 5 | Testing for tensile cracks | - | No cracks | No cracks |
| 6 | Shore hardness | - | 80±5 | 80-85 |
| 7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| 8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| 9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
| 10 | Elongation at break | % | ≥2.5 | ≥2.6 |
| 11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| 12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| 13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| 14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| 15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1.Sample water content less than 0.2% by weight.
2.Norm laboratory condition:(23±2)ºC and (50±10)% relative humidity.
3.The specifications marked with "a" only applies to I-shape strip otherwise, the specifications concluded between supplier and buyer through consultation, shall be written in contract or purchase order.
Advantage:
- High-quality Nylon/PA66 granules reinforced with fiberglass
- Meets national standards for exceptional performance
- Made from PA66 resin with added glass fiber, flame retardants, and additives
- Twin-screw extrusion blending process ensures superior quality
- Super toughened for enhanced strength and durability
- Excellent chemical resistance and insulation properties
- Perfect for material engineering, nylon profiles, and recycled products
Application:
Specially used in thermal break strips, thermal bridge, heat insulation bar, etc.
Packaging & Delivery:
Packaging details:25kg/bag
Delivery details: shipped in 5-8 working days after receiving the payment
Please feel free to contact us if you have any questions.
Address:Jinfeng Town, Zhangjiagang City, Jiangsu Province, China
Product Tags:
|
|
Plastic Raw Material Extruding Grade Nylon PA6 Pellets For Window Thermal Break Profile Images
|